GB/T 44295-2024 多层印制板用环氧E玻纤布粘结片

ICS31.180

CCSL30

中华人民共和国国家标准

GB/T44295—2024

多层印制板用环氧E玻纤布粘结片

EpoxidewovenE⁃glassprepregformultilayerprintedboards

［IEC61249⁃4⁃1：2008Materialsforprintedboardsandotherinterconnecting

structures—Part4⁃1：Sectionalspecificationsetforprepregmaterials，

unclad（forthemanufactureofmultilayerboards）—Epoxidewoven

E⁃glassprepregofdefinedflammability，MOD］

2024⁃08⁃23发布2024⁃12⁃01实施

国家市场监督管理总局

发布

国家标准化管理委员会

GB/T44295—2024

目次

前言··························································································································Ⅲ

1范围·······················································································································1

2规范性引用文件········································································································1

3术语和定义··············································································································1

4材料和结构··············································································································1

5性能要求·················································································································2

6尺寸·······················································································································4

7质量保证·················································································································5

8包装和标识··············································································································6

9储存期····················································································································6

10订单信息···············································································································6

附录A（资料性）本文件与IEC61249⁃4⁃1：2008的结构编号对照一览表···································7

附录B（资料性）本文件与IEC61249⁃4⁃1：2008技术差异及其原因·········································9

附录C（规范性）检验方法要求·····················································································11

附录D（规范性）比例流动厚度试验方法·········································································12

附录E（规范性）熔融黏度试验方法···············································································15

附录F（规范性）差示扫描量热法（DSC）测玻璃化温度·······················································17

参考文献····················································································································19

图D.1层压前比例流动厚度试样···················································································13

图D.2比例流动厚度试样的测量点················································································13

图E.1熔融黏度曲线图示例··························································································16

图F.1差示扫描量热法（与玻璃转变相关的特征转变点）······················································18

表1垂直燃烧等级·······································································································4

表2储存条件和储存期·································································································6

表A.1本文件与IEC61249⁃4⁃1：2008的结构编号对照情况···················································7

表B.1本文件与IEC61249⁃4⁃1：2008技术差异及其原因·······················································9

表C.1检验方法要求··································································································11

表D.1不同厚度的E玻纤布叠合层数·············································································12

表E.1不同的旋转速度以下的黏度值··············································································15

Ⅰ

GB/T44295—2024

前言

本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规

定起草。

本文件修改采用IEC61249⁃4⁃1：2008《印制板及其他互连结构用材料第4⁃1部分：不覆铜的预浸

料分规范多层印制电路板用限定燃烧性环氧E玻纤布粘结片》。

本文件与IEC61249⁃4⁃1：2008相比，在结构上有较多调整，两个文件之间的结构编号对照一览表

见附录A。

本文件与IEC61249⁃4⁃1：2008相比，存在较多技术差异，在所涉及的条款的外侧页边空白位置用

垂直单线（|）进行了标识。这些技术差异及其原因一览表见附录B。

本文件做了下列编辑性改动：

——将IEC61249⁃4⁃1：2008的第3章和第5章中的悬置段，分别移至本文件的4.1和6.1中；

——删除了第1章中错误逻辑的语句，并重新进行了表述；

——将第6章的标题由“交付状态”改为“尺寸”，使标题与内容更贴切；

——由于IEC61249⁃4⁃1：2008的4.2.4引用的IEC61189⁃2的方法2M26没有对应的国内同类标

准，为了使用方便，将引用的IEC61189⁃2的方法2M26内容转化为附录D（规范性）比例流动

厚度试验方法；

——由于IEC61249⁃4⁃1：2008的4.2.5引用的IEC61189⁃2的方法2C09没有对应的国内同类标

准，为了使用方便，将引用的IEC61189⁃2的方法2C09内容转化为附录E（规范性)熔融黏度

试验方法。

请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。

本文件由中华人民共和国工业和信息化部提出。

本文件由全国印制电路标准化技术委员会（SAC/TC47）归口。

本文件起草单位：陕西生益科技有限公司、中国电子技术标准化研究院、广东生益科技股份有限公

司、浙江华正新材料股份有限公司、江苏生益特种材料有限公司、苏州生益科技有限公司、江西生益科

技有限公司、常熟生益科技有限公司。

本文件主要起草人：张记明、刘洁、刘申兴、曹易、蔡建伟、谭育虎、何小玲、马海鱼、陈佳、王金瑞、

袁告、罗鹏辉、王隽、邢燕侠。

Ⅲ

GB/T44295—2024

多层印制板用环氧E玻纤布粘结片

1范围

本文件规定了E玻纤布增强双官能环氧粘结片（以下简称“粘结片”）的材料和结构、性能要求、尺

寸、质量保证及包装和标识、储存期、订单信息。

本文件适用于制造IEC62326⁃4多层印制板时用以粘结IEC61249⁃2⁃7类型的层压板，该材料可

用于粘结多层印制电路板。

本文件限定了粘结片的燃烧性（垂直燃烧试验），其阻燃效果是通过聚合物型含溴阻燃剂实现的，

层压后的玻璃化温度不低于120℃。

2规范性引用文件

下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中，注日期的引用文

件，仅该日期对应的版本适用于本文件；不注日期的引用文件，其最新版本（包括所有的修改单）适用于

本文件。

GB/T2036印制电路术语

GB/T4722—2017印制电路用刚性覆铜箔层压板试验方法

GB/T16483化学品安全技术说明书内容和项目顺序

GB/T19000质量管理体系基础和术语（GB/T19000—2016，ISO9000：2015，IDT）

GB/T24001环境管理体系要求及使用指南（GB/T24001—2016，ISO14001：2015，IDT）

GB/T33015—2016多层印制板用粘结片通用规则

GB/T33016—2016多层印制板用粘结片试验方法

IEC61249⁃6⁃3印制板及其他互连结构用材料第6⁃3部分：增强材料分规范印制板用E玻纤布规范

（Materialsforprintedboardsandotherinterconnectingstructures—Part6⁃3：Sectionalspecificationsetforre⁃

inforcementmaterials—Specificationforfinishedfabricwovenfrom“E”glassforprintedboards）

3术语和定义

GB/T2036界定的术语和定义适用于本文件。

4材料和结构

4.1结构

粘结片是由环氧树脂浸渍的E玻纤布构成，半固化至B阶。

4.2增强材料

增强材料为符合IEC61249⁃6⁃3规定的E玻纤布。

1