GB/T 4100-2006 陶瓷砖

ICS91.100.25

31

Q三疡8

中华人民共和国国家标准

GB/T4100-2006

代替GB/T4100.1^-4100.5-1999

陶瓷砖

Ceramictiles

(ISO13006:1998Ceramictiles-

DefinitionsIclassification,characteristicsandmarking,MOD)

2006-02-07发布2006-09-01实施

中华人民共和国国家质量监督检验检疫总局

中国国家标准化管理委员会发布

GB/T4100-2006

目次

前言··················································································································……I

1范围···············································································································……1

2规范性引用文件·······························································································…·…1

3术语和定义······································································································……2

4分类···············································································································……4

4.1分类方法······································································································……4

4.2按成型方法分类·····························································································……5

4.3按吸水率(E)分类··························································································……5

5性能···············································································································……5

6抽样和接收条件·······························································································……6

7要求··············································································································……6

8标志和说明····································································································……6

8.1标志············································································································……6

8.2产品特性······································································································……6

8.3说明书·········································································································……6

9订货···············································································································……7

附录A(规范性附录)挤压陶瓷砖E<3aoAI类·························································……8

附录B(规范性附录)挤压陶瓷砖3ao<EG6/aoAIIa类—第1部分···························……11

附录C(规范性附录)挤压陶瓷砖3oo<E<6ooA]1a类—第2部分···························……14

附录D(规范性附录)挤压陶瓷砖6/ao<E<IOaoAIIb类—第1部分························……17

附录E(规范性附录)挤压陶瓷砖6aa<E<l0oaAIIb类—第2部分·······················…·…20

附录F(规范性附录)挤压陶瓷砖E>10%AU[类······················································……23

附录G(规范性附录)干压陶瓷砖E<0.5%BIa类—瓷质砖····································……26

附录H(规范性附录)干压陶瓷砖。.5%<E<3%BIb类—拓瓷砖···························……29

附录J(规范性附录)干压陶瓷砖3%<E<6%BU.类—细灯砖······························……32

附录K(规范性附录)干压陶瓷砖6%<E<10%BIIb类—拓质砖···························……35

附录L(规范性附录)干压陶瓷砖E>10%B班类—陶质砖·······································……38

附录M(规范性附录)磨擦系数的测定·····································································……41

附录N(资料性附录)包装标记使用规定··································································……44

附录P(资料性附录)有釉地砖耐磨性分级·······························································……45

附录Q(资料性附录)试验方法·········，···································································……46

GB/T4100-2006

月q吕

本标准修改采用ISO13006:199M陶瓷砖—定义、分类、性能和标记)}(英文版)。

为了更适合我国国情，本标准在采用ISO13006:1998时进行了修改，本标准与ISO13006:1998的

主要差异如下:

—标准名称“陶瓷砖—定义、分类、性能和标记”修改为“陶瓷砖”;

—删除了国际标准的前言;

—将1中“…性能和标记”修改为“…性能、抽样和接收条件、技术要求和试验方法、标志和说明、

订货”;

—将国际标准中的“参照标准”修改为“规范性引用文件”，并将所引用的国际标准用采用该国际

标准的国家标准代替;

—增加了“瓷质砖、烙瓷砖、细KG砖、拓质砖、陶质砖”的定义;

—在附录G(规范性附录)中增加了对大规格产品尺寸偏差的规定;

—在附录G(规范性附录)中增加了对抛光砖的规定。

本标准代替GB/T4100.1-1999《干压陶瓷砖第1部分:瓷质砖(吸水率E毛0.5%)),

GB/T4100.2-1999《干压陶瓷砖第2部分:炫瓷砖(吸水率。.5%<EG3%)),GB/T4100.3-1999

《干压陶瓷砖第3部分:细拓砖(吸水率3%<E簇60o))),GB/T4100.4-1999《干压陶瓷砖第4部

分:场质砖(吸水率6%<E毛10%))),GB/T4100.5-1999《干压陶瓷砖第5部分:陶质砖(吸水率

E>10%)))0

本标准与GB/T4100.1-1999,GB/T4100.2-1999,GB/T4100.3-1999,GB/T4100.4-1999,

GB/T4100.5-1999相比主要变化如下:

—增加了对挤压陶瓷砖的要求;

—删除了干压烙瓷砖大规格产品尺寸允许偏差的要求;

—修改了第3章“定义”;

—取消了产品等级;

—增加了第4章分类和第5章性能;

—将"6检验规则”修改为“6抽样和接收条件”;

—将"4技术要求”和“5试验方法”合并为“7要求”，且编排格式与国际标准对应，分别列人

相应附录中;

—将“8包装、运输、贮存和订货”修改为“9订货”;

—将GB/T4100.1-1999附录A((陶瓷砖磨擦系数的测定》修改为附录M,删除了动滑块法和

倾斜平台法，保留了静滑块法。

本标准的附录A、附录B、附录C、附录D、附录E、附录F、附录G、附录H、附录J,附录K、附录L,

附录M为规范性目录;附录N、附录P、附录Q为资料性附录

用测量值或计算值判定本标准中的极限值时，采用修约值比较法。

本标准自实施之日起，JC/T457.3-2002《挤压陶瓷砖第3部分:细烙砖(吸水率3%<E(

6%))),JC/T457.4-2002《挤压陶瓷砖第4部分:灯质砖(吸水率6%<EGIO%)))作废。

本标准由中国建筑材料工业协会提出。

本标准由全国建筑卫生陶瓷标准化技术委员会归口。

本标准起草单位:咸阳陶瓷研究设计院。

GB/T4100-2006

本标准参加起草单位:佛山石湾鹰牌陶瓷有限公司、广东蒙娜丽莎陶瓷(集团)有限公司、佛山市兴

辉陶瓷有限公司、杭州诺贝尔集团有限公司。

本标准参加起草人:刘幼红、王博、李直、钟应洲、张旗康、陈洪再、李莹。

本标准所代替标准的历次版本发布情况为:

—GB/T11947-1989;

—GB/T4100-1992;

-GB/T4100.1-1999,GB/T4100.2-1999,GB/T4100.3-1999,GB/T4100.4-1999,

GB/T4100.5-1999.

GB/T4100-2006

陶瓷砖

范围

本标准规定了陶瓷砖的定义、分类、性能、抽样和接收条件、技术要求和试验方法、标志和说明、

订货。

2规范性引用文件

下列文件中的条款通过本标准的引用而成为本标准的条款。凡是注日期的引用文件，其随后所有

的修改单(不包括勘误的内容)或修订版均不适用于本标准，然而，鼓励根据本标准达成协议的各方研究

是否可使用这些文件的最新版本。凡是不注日期的引用文件，其最新版本适用于本标准。

GB/T3810.1陶瓷砖试验方法第1部分:抽样和接收条件(GB/T3810.1-2006,ISO10545-1:

1995,MOD)

GB/T3810.2陶瓷砖试验方法第2部分:尺寸和表面质量的检验(GB/T3810.2-2006,

ISO10545-2:1995,MOD)

GB/T3810.3陶瓷砖试验方法第3部分:吸水率、显气孔率、表观相对密度和容重的测定

(GB/T3810.3-2006,ISO10545-3:1995,MOD)

GB/T3810.4陶瓷砖试验方法第4部分:断裂模数和破坏强度的测定(GB/T3810.4-2006,

ISO10545-4:1994,IDT)

GB/T3810.5陶瓷砖试验方法第5部分:用恢复系数确定砖的抗冲击性(GB/T3810.5-

2006,ISO10545-5:1996,IDT)

GB/T3810.6陶瓷砖试验方法第6部分:无釉砖耐磨深度的测定(GB/T3810.6-2006,

ISO10545-6:1995,IDT)

GB/T3810.7陶瓷砖试验方法第7部分:有釉砖表面耐磨性的测定(GB/T3810.7-2006,

ISO10545-7:1996,IDT)

GB/T3810.8陶瓷砖试验方法第8部分:线性热膨胀的测定(GB/T3810.8-2006,

ISO10545-8:1994,IDT)

GB/T3810.9陶瓷砖试验方法第9部分:抗热震性的测定(GB/T3810.9-2006,

ISO10545-9:1994,IDT)

GB/T3810.10陶瓷砖试验方法第10部分:湿膨胀的测定(GB/T3810.10-2006,

ISO10545-10:1995,IDT)

GB/T3810.11陶瓷砖试验方法第11部分:有釉砖抗釉裂性的测定(GB/T3810.11-2006,

ISO10545-11:1994,IDT)

GB/T3810.12陶瓷砖试验方法第12部分:抗冻性的测定(GB/T3810.12-2006,

ISO10545-12:1995,IDT)

GB/T3810.13陶瓷砖试验方法第13部分:耐化学腐蚀性的测定(GB/T3810.13-2006,

ISO10545-13:1995,IDT)

GB/T3810.14陶瓷砖试验方法第14部分:耐污染性的测定(GB/T3810.14-2006,

ISO10545-14:1995,IDT)

GB/T3810.15陶瓷砖试验方法第15部分:有釉砖铅和锅溶出量的测定(GB/T3810.15-

2006,ISO10545-15:1995,IDT)

GB/T4100-2006

GB/T3810.16陶瓷砖试验方法第16部分:小色差的测定(GB/T3810.16-2006,ISO10545-

16:1999,IDT

GB/T13891建筑饰面材料镜向光泽度测定方法

3术语和定义

下列术语和定义适用于本标准。

3门

陶瓷砖ceramictiles

由粘土和其他无机非金属原料制造的用于覆盖墙面和地面的薄板制品，陶瓷砖是在室温下通过挤

压或干压或其他方法成型，干燥后，在满足性能要求的温度下烧制而成。砖是有釉(GL)或无釉(UGL)

的，而且是不可燃、不怕光的。

3.2

釉glaze

不透水的玻化覆盖层。

3.3

底釉engobedsurface

覆盖在粘土坯表面的透水或不透水无光饰面。

注:表面只有底釉的砖被当作无釉砖。

3.4

抛光面polishedsurface

无釉陶瓷砖最后工序经机械研磨、抛光使砖所具有的光泽表面。

3.5

挤压砖(A)extrudedtiles

挤压砖是将可塑性坯料经过挤压机挤出成型，再将所成型的泥条按砖的预定尺寸进行切割。

注1:这些产品分为精细的或普通的，主要是由它们的性能来决定的

注2:挤压砖的习惯术语是用来描述劈离砖和方砖的，通常分别是指双挤压砖和单挤压砖，方砖仅指吸水率不超过

6%的挤压砖。

3.6

干压砖(B)dry-pressedtiles

干压砖是将混合好的粉料置于模具中于一定压力下压制成型的。

3.7

其他方法成型的砖(C)tilesmadebyotherprocesses

用挤或压以外方法成型的陶瓷砖

注:这类砖不包含在本标准中。

3.8

瓷质砖porcelaintiles

吸水率(E_)不超过。.5%的陶瓷砖

3.9

炳瓷砖stonewareporcelaintiles

吸水率(E)大于。.5%，不超过3%的陶瓷砖

3.10

细拓砖finestonewaretiles

吸水率(E)大于3%，不超过6%的陶瓷砖

GB/T4100-2006

3.11

拓质砖stonewaretiles

吸水率(E)大于6%，不超过10%的陶瓷砖。

3.12

陶质砖fineearthenwaretiles

吸水率(E)大于10%的陶瓷砖。

3.13

吸水率(E)waterabsorption

用质量分数表示，按GB/T3810.3规定测定。

3.14

rEl隔凸缘(见图2)spacerlugs

带有凸缘的砖，便于使沿直线铺贴的两块砖之间的接缝宽度不超过规定的要求。

注1:两块砖之间连接位置的凸缘由水泥砂浆覆盖使凸缘不暴露在外。

注2:由制造者提供工作尺寸，可以按相同情况将千压成型砖加工间隔凸缘。

3.15

尺寸描述(见图1,图2)descriptionofsizes

注:这里描述的尺寸只适用于矩形砖，对于非矩形砖可以采用相应的最小矩形的尺寸。

3.15.1

名义尺寸nominalsize

用来统称产品规格的尺寸。

3.15.2

工作尺寸(W)worksize

按制造结果而确定的尺寸，实际尺寸与其之间的差应在规定的允许偏差之内。

注:工作尺寸包括长、宽、厚

3.15.3

实际尺寸actualsize

按照GB/T3810.2中规定的方法测得的尺寸。

3.15.4

配合尺寸(C)coordinatingsize

工作尺寸加上连接宽度

3.15.5

模数尺寸modularsize

模数尺寸包括了尺寸为MOM-100mm),2M,3M和5M以及它们的倍数或分数为基数的砖，不

包括表面积小于9000mm,的砖。

3.15.6

非模数尺寸non-modularsizes

不以模数M为基数的尺寸。

3.15.7

公差tolerance

在尺寸允许范围之内的偏差。

GB/T4100-2006

配合尺寸(C)=工作尺寸(W)+连接宽度(J)

工作尺寸(W)=可见面(a),(b)和厚度(d)的尺寸

图1砖的尺寸

配合尺寸(0=工作尺寸(W)+连接宽度J()

工作尺寸(W)二可见面(a),(b)和厚度(d)的尺寸

图2带有间隔凸缘的砖

4分类

4.1分类方法

按照陶瓷砖的成型方法和吸水率(见3.13和表1)进行分类，这种分类与产品的使用无关。

表1陶瓷砖按成型方法和吸水率分类表

成型方法I类na类Qb类皿类

E<3%3%<F(6%6%<E<10%E>10%

A11a1类，AIIbl类，

AI类(见附录B)(见附录D)Am类

A(挤压)

(见附录A)(见附录F)

Apa2类a，Allb2类a，

(见附录C(见附录E)

BIa类

瓷质砖E<0.5肠

BQa类Bj/b类Bm类句

(见附录G)

B(干压)细拓砖灯质砖陶质砖

BIb类

(见附录J)(见附录K)(见附录L)

拓瓷砖。.5%<E<3%

(见附录H)

C(其他)C工类亡，C[/a类)cCHb类。C皿类。

a)AHa类和AHb类按照产品不同性能分为两个部分。

bB班类仅包括有釉砖，此类不包括吸水率大于10%的干压成型无釉砖。

0本标准中不包括这类砖。

GB/T4100-2006

42按成型方法分类

A挤压砖((3.5);

B干压砖(3.6);

C其他方法成型的砖((3.7)。

4.3按吸水率(E)分类

按吸水率分为以下三类:

4.3.1低吸水率砖(I类),E<3%

工类干压砖还可以进一步分为:

(a)E<0.50o(BIa类);

(b)0.5%<E<3%(BIb类)。

4.3.2中吸水率砖(II类),3%<E<10%

11类挤压砖还可一步分为:

(a)3%<E<6%(AI[a类，第1部分和第2部分);

(b)6%<E<10%(AIIb类，第1部分和第2部分)。

n类干压砖还可一步分为:

(a)3%<E<6%(BIIa类);

(b)6%<E<10%(BUb类)。

4.3.3高吸水室砖(m谁).E>10%.

5性能

在表2中列出了不同用途陶瓷砖的产品性能要求。

表2不同用途陶瓷砖的产品性能要求

性能地砖墙砖试验方法

尺寸和表面质量室内室外室内室外标准号

长度和宽度XXXXGB/T3810.2

厚度XXXXGB/T3810.2

边直度XXXXGB/T3810.2

直角度XXXXGB/T3810.2

表面平整度(弯曲度和翘曲度)XXXXGB/T3810.2

物理性能室内室外室内室外标准号

吸水率XXXXGB/T3810.3

破坏强度XXXXGB/T3810.4

断裂模数XXXXGB/T3810.4

无釉砖耐磨深度XXGB/T3810.6

有釉砖表面耐磨性XXGB/T3810.7

线性热膨胀司XXXXGB/T3810.8

抗热震性的XXXXGB/T3810.9

有釉砖抗釉裂性XXXXGB/T3810.11

抗冻性日XXGB/T3810.12

磨擦系数XX附录M

GB/T4100-2006

表2(续)

性能地砖墙砖试验方法

物理性能室内室外室内室外标准号

湿膨胀的XXXXGB/T3810.10

小色差的XXXXGB/T3810.16

抗冲击性巴，XXGB/T3810.5

抛光砖光泽度XXXXGB/T13891

化学性能室内室外室内室外标准号

有釉砖耐污染性XXXXGB/T3810.14

无釉砖耐污染性的XXXXGB/T3810.14

耐低浓度酸和碱化学腐蚀性XXXXGB/T3810.13

耐高浓度酸和碱化学腐蚀性的XXXXGB/T3810.13

耐家庭化学试剂和游泳池盐类化学

XXXXGB/T3810.13

腐蚀性

有釉砖铅和锅的溶出量幻XXXXGB/T3810.15

a)见附录Q试验方法

b)砖在有冰冻情况下使用时。

6抽样和接收条件

抽样和接收条件应符合GB/T3810.1的要求。

7要求

各类陶瓷砖的尺寸、表面质量、物理性能和化学性能的技术要求应符合附录A~附录L中的相应

规定

8标志和说明

8.1标志

砖或其包装上应有下列标志:

a.制造商的标记和/或商标以及产地;

b.质量标志;

c.砖的种类及执行本标准的相应附录;

d.名义尺寸和工作尺寸，模数(M)或非模数;

e.表面特性，如有釉(GL)或无釉(UG工_)。

8.2产品特性

对用于地面的陶瓷砖，应报告以下特性:

a.按本标准附录M规定所测得的摩擦系数;

b.有釉砖的耐磨性级别。

注:按附录P规定的耐磨性级别。

8.3说明书

产品说明书中应包括下列内容:

GB/T4100-2006

a.成型方法;

b.陶瓷砖类别及执行本标准的相应附录;

c.名义尺寸和工作尺寸，模数(M)和非模数;

d.表面特性，如，有釉(GI.)或无釉(UGL)o

例如:

精细挤压砖，GB/T4100-2006附录A

AIM25cmX12.5cm(W240mmX115mmX10mm)GL

普通挤压砖，GB/T4100-2006附录A

A115cmX15cm(W150mmX150mmX12.5mm)UGL

9订货

在订货时，如尺寸、厚度、表面特征、颜色、外观、有釉砖耐磨性级别以及其他性能均应与相关方协商

一致

GB/T4100-2006

附录A

(规范性附录)

挤压陶瓷砖E<3%AI类

A.1要求

该类产品的尺寸、表面质量、物理性能和化学性能的技术要求应符合表A.1的规定。

表A.1挤压陶瓷砖技术要求(E镇3%,Al类)

技术要求

试验方法

尺寸和表面质量精细普通

每块砖((2条或4条边)的平均尺寸相对于工作尺寸士1.0%,士2.o%,

GB/T3810.2

(W)的允许偏差/%最大士Zmm最大士4mm

长

度每块砖((2条或4条边)的平均尺寸相对于10块砖(20士1.0%士1.5%GB/T3810.2

和条或40条边)平均尺寸的允许偏差/肠

宽

度制造商选择工作尺寸应满足以下要求

a.模数砖名义尺寸连接宽度允许在((3.11)mm之间。。GB/T3810.2

b.非模数砖工作尺寸与名义尺寸之间的偏差不大于士3mm

厚度

a.厚度由制造商确定。士10%士10%GB/T3810.2

b.每块砖厚度的平均值相对于工作尺寸厚度的允许偏差/%

边直度.(正面)

士0.5写士0.6%GB/T3810.2

相对于工作尺寸的最大允许偏差/%

直角度卜，

士1.0%士1.0肠GB/T3810.2

相对于工作尺寸的最大允许偏差/%

a.相对于由工作尺寸计算的对角线

士0.5%士1.5%GB/T3810.2

的中心弯曲度

表面平整度

b.相对于工作尺寸的边弯曲度士0.5%士1.5%GB/T3810.2

最大允许偏差/%

c.相对于由工作尺寸计算的对角线

士0.8%士1.5%GB/T3810.2

的翘曲度

至少95%的砖主要区域无明显

表面质量。GB/T3810.2

缺陷

物理性能精细普通试验方法

平均值毛3.0%,平均值镇3.。%，

吸水率h，，质量分数GB/T3810.3

单值G3.3%单值簇3.3%

a.厚度)7.smm)1100>1100GB/T3810.4

破坏强度/N

b.厚度<7.5mm>600>600GB/T3810.4

断裂模数/(N/mm')(MPa)平均值妻23，单平均值)23，单

GB/T3810.4

不适用于破坏强度李3000N的砖值)18值李18

GB/T4100-2006

表A.1(续)

技术要求

试验方法

物理性能精细普通

a.无釉地砖耐磨损体积/mm'(275簇275GB/T3810.6

耐磨性

b.有釉地砖表面耐磨性11报告陶瓷砖耐磨性级别和转数GB/T3810.7

线性热膨胀系数e〕从环境温度到1000C见附录QGB/T3810.8

抗热震性司见附录QGB/T3810.9

有釉砖抗釉裂性1，经试验应无釉裂GB/T3810.11

抗冻性曰见附录QGB/T3810.12

制造商应报告陶瓷地砖的摩擦系数

地砖摩擦系数附录M

和试验方法

湿膨胀/)mm/m见附录QGB/T3810.10

小色差曰见附录QGB/T3810.16

抗冲击性曰见附录QGB/T3810.5

化学性能精细普通试验方法

a.有釉砖最低3级最低3级GB/T3810.14

耐污染性

b.无釉砖曰见附录QGB/T3810.14

耐低浓度酸和碱

制造商应报告耐制造商就报告耐

a有釉砖GB/T3810.13

化学腐蚀性等级化学腐蚀性等级

b.无釉砖妒

抗化学腐蚀性耐高浓度酸和碱的见附录QGB/T3810.13

耐家庭化学试剂和游泳池盐类

a.有釉砖不低于GB级不低于GB级GB/T3810.13

b.无釉砖砂不低于UB级不低于UB级

铅和锅的溶出量e，见附录QGB/T3810.15

a)以非公制尺寸为基础的习惯用法也可用在同类型砖的连接宽度上.

b)不适用于有弯曲形状的砖

c)在烧成过程中，产品与标准板之间的微小色差是难免的。本条款不适用于在砖的表面有意制造的色差(表面

可能是有釉的、无釉的或部分有釉的)或在砖的部分区域内为了突出产品的特点而希望的色差。用于装饰目

的的斑点或色斑不能看作为缺陷。

山有釉地砖耐磨性分级可参照本标准附录P规定。

e)表中所列见“附录Q'I涉及项目不是所有产品都必检的，是否有必要对这些项目进行检验应按本标准附录Q

的规定确定。

f)制造商对于为装饰效果而产生的裂纹应加以说明，这种情况下，GB/T3810.11规定的釉裂试验不适用。

a)如果色泽有微小变化，不应算是化学腐蚀.

h)吸水率最大单个值为0.5%的砖是全玻化砖(常被认为是不吸水的)

A.2抽样和接收条件

抽样和接收条件应符合GB/T3810.1的要求

GB/T4100-2006

A.3标志和说明

A31标志

砖或其包装上应有下列标志:

a.制造商的标记和/或商标以及产地;

b.质量标志;

c.砖的种类及执行本标准的相应附录;

d.名义尺寸和工作尺寸，模数(M)或非模数;

c.表面特性，如有釉(GL)或无釉(UGIJ

A.3.2产品特性

对用于地面的陶瓷砖，应报告以下特性:

a.按本标准附录M规定所测得的摩擦系数;

b有釉砖的耐磨性级别。

注:按附录P规定的耐磨性级别

A.3.3说明书

产品说6K书中应包括下列内容:

a.成型方法;

b.陶瓷砖类别及执行本标准的相应附录;

c.名义尺寸和工作尺寸，模数(M)和非模数;

d.表面特性，如，有釉(GI,)或无釉(UGL)o

例如:

精细挤压砖，GB/T4100--2006附录A

AIM25cmX12.5cm(W240mmX115mmX10mm)GI

普通挤压砖，GB/T4100-2006附录A

AI15cmX15cm(W150mmX150mmX12.5mm)UGL

A.4订货

在订货时，如尺寸、厚度、表面特征、颜色、外观、有釉砖耐磨性级别以及其他性能均应与相关方协商

一致。

GB/T4100-2006

附录B

(规范性附录)