GB/T 7314-2005 金属材料 室温压缩试验方法

ICS77.040.10

H22荡黯

中华人民共和国国家标准

GB/T7314-2005

代替GB/T7314-1987

金属材料室温压缩试验方法

Metallicmaterials-Compressiontestingatambienttemperature

2005-05-13发布2005-10-01实施

中华人民共和国国家质量监督检验检疫总局发布

中国国家标准化管理委员会

GB/T7314-2005

目次

前言··················································································································……工

1范围···············································································································……1

2规范性引用文件·······················································································.········……1

3原理···············································································································……1

4术语和定义······································································································……1

5符号和说明······································································································……3

6试样···，··············，············································，·················，····，····，····，·····】，····，··……4

7试验设备································、········································································……6

8试验条件·········································································································……9

9性能测定·········································································································……9

10性能测定结果数值的修约······································································……13

11性能测定结果的不确定度························································……13

12试验结果处理····。···························································································……13

13试验报告······································································································……13

附录A(资料性附录)本标准与旧标准性能名称和符号对照··。·······································……15

GB/T7314-2005

前言

本标准修改采用美国材料与试验协会标准ASTME9-89a(2000)((金属材料室温压缩试验方法》。

本标准与ASTME9-89a(2000)的差异如下:

—采用国际单位制;

—删去ASTME9-89a(2000)的第4章试验方法概述;

—删去第5章意义和用途;

—删去ASTME9-89a(2000)的第12章关键词;

—删去ASTME9-89a(2000)的附件和参考文献;

—增加原理(本标准第3章);

—增加符号和说明(本标准第5章);

—增加性能测定结果的修约(本标准第10章);

—增加试验结果处理(本标准第12章)。

本标准代替GB/T7314-1987《金属压缩试验方法》。本标准与GB/T7314-1987相比，在技术内

容上主要有如下变化:

—增加了规范性引用文件(见第2章);

—增加了原理(见第3章);

—修改了术语和定义(1987年版的1.1，本版的第4章);

—修改了符号和说明(1987年版的1.2，本版的第5章);

—修改了引伸计使用级别(1987年版的3.6，本版的7.6);

—修改了屈服强度的测定(1987年版的5.5，本版的9.5);

—增加了塑性材料的抗压强度测定内容(见4.10,9.6);

—增加了可使用自动测试系统的规定(见9.2.3,9.3.3,9.4.2,9.5.3,9.6,9.7);

—增加了性能测定结果的不确定度(见第n章);

—增加了试验报告(见第13章);

—增加了资料性附录“本标准与旧标准性能名称和符号对照”(见附录A),

本标准的附录A是资料性附录。

本标准由中国钢铁工业协会提出。

本标准由全国钢标准化技术委员会归口。

本标准起草单位:国防科学技术大学。

本标准主要起草人:郑文龙、刘甫、雷勇军。

本标准所代替标准的历次版本发布情况为:

—GB/T7314-1987.

GB/T7314-2005

金属材料室温压缩试验方法

范围

本标准规定了金属材料室温压缩试验方法的原理、定义、符号和说明、试样及其尺寸测量、试验设

备、试验要求、性能测定、测定结果数值修约和试验报告

本标准适用于测定金属材料在室温下单向压缩的规定非比例压缩强度、规定总压缩强度、上压缩屈

服强度、下压缩屈服强度、压缩弹性模量及抗压强度。

2规范性引用文件

下列文件中的条款通过本标准的引用而成为本标准的条款。凡是注日期的引用文件，其随后所有

的修改单(不包括勘误的内容)或修订版均不适用于本标准，然而，鼓励根据本标准达成协议的各方研究

是否可使用这些文件的最新版本。凡是不注日期的引用文件，其最新版本适用于本标准。

GB/T817。数值修约规则

GB/T12160单轴试验用引伸计的标定(GB/T12160-2002,ISO9513:1999,Metallicmateri-

als-Calibrationofextensometersusedinuniaxialtesting,IDT)

GB/T16825.1静力单轴试验机的检验第1部分:拉力和(或)压力试验机测力系统的检验与校

准(GB/T16825.1-2002,ISO7500-1:1999,Metallicmaterials-Verificationofstaticuniaxialtesting

machines-Part1:Tension/compressiontestingmachines-Verifcationandcalibrationoftheforce-

measuringsystem,IDT)

原理

试样受轴向递增的单向压缩力，且力和变形可连续地或按有限增量进行检测，测定第4章定义的一

项或几项压缩力学性能。

术语和定义

下列术语和定义适用于本标准。

4.1

屈曲buckling

除通过材料的压溃方式引起压缩失效外，以下几种方式也可能发生压缩失效:①由于非轴向加力

而引起柱体试样在其全长度上的弹性失稳;②柱体试样在其全长度上的非弹性失稳;③板材试样标距

内小区域上的弹性或非弹性局部失稳;④试样横截面绕其纵轴转动而发生的扭曲或扭转失效。这几种

失效类型统称为屈曲。

4.2

单向压缩singlecompression

试样受轴向压缩时，弯曲的影响可以忽略不计，标距内应力均匀分布，且在试验过程中不发生屈曲。

4.3

试样原始标距specimenoriginalgaugelength

L,

1

GB/T7314-2005

用以测量试样变形的那一部分原始长度，此长度应不小于b或d,

4.4

实际压缩力realcompressionforce

F

压缩过程中作用在试样轴线方向上的力;对夹持在约束装置中进行试验的板状试样，是标距中点处

扣除摩擦力后的力。

4.5

摩擦j7frictionforce

F,

被约束装置夹持的试样，在加力时，两侧面与夹板之间产生的摩擦力。

4.6

压缩应力compressionstress

试验过程中试样的实际压缩力F与其原始横截面积5。的比值。

4.7

规定非比例压缩强度proofstrength,non-proportionalcompression

Rp

试样标距段的非比例压缩变形达到规定的原始标距百分比时的压缩应力。表示此压缩强度的符号

应以下脚标说明，例如凡.‘。，、凡。:分别表示规定非比例压缩应变为0.01Yo,0.2写时的压缩应力。

4.8

规定总压缩强度proofstrength,totalcompression

R,

试样标距段的总压缩变形(弹性变形加塑性变形)达到规定的原始标距百分比时的压缩应力。表示

此压缩强度的符号应附以下脚标说明，例如R,.,.,表示规定总压缩应变为l.5%时的压缩应力。

4.9

压缩屈服强度compressiveyieldstrength

当金属材料呈现屈服现象时，试样在试验过程中达到力不再增加而仍继续变形所对应的压缩应力，

应区分上压缩屈服强度和下压缩屈服强度。

4.9.1

上压缩屈服强度uppercompressiveyieldstrength

R-

试样发生屈服而力首次下降前的最高压缩应力。

4.9.2

下压缩屈服强度lowercompressiveyieldstrength

Re,

屈服期间不计初始瞬时效应时的最低压缩应力。

4.10

抗压强度compressivestrength

R.,

对于脆性材料，试样压至破坏过程中的最大压缩应力。

对于在压缩中不以粉碎性破裂而失效的塑性材料，则抗压强度取决于规定应变和试样几何形状。

4.11

压缩弹性模fcompressivemodulusofelasticity

E

试验过程中，应力应变呈线性关系时的压缩应力与应变的比值。

GB/T7314-2005

5符号和说明

本标准所用符号和相应的说明见表

表1符号和说明

符号单位说明

试样

amnl试样原始厚度

bmm试样原始宽度

dmm试样原始直径

Lnln1试样长度

L,mm试样原始标距

HInlll约束装置的高度

h刀11】」板材试样无约束部分的长度

Somm'试样原始横截面积